| 周丽君,刘强,单振,吴霞.炭黑N134在全钢载重子午线轮胎胎面胶中的应用[J].橡胶科技,2015,13(5):30-33. |
二维码（扫一下试试看！） |
| 炭黑N134在全钢载重子午线轮胎胎面胶中的应用 |
| Application of Carbon Black N134 in the Tread Compound of TBR Tire |
| |
| DOI： |
| 中文关键词: 炭黑N134 炭黑N234 全钢载重子午线轮胎 胎面胶 抗硫化返原剂 耐磨性能 |
| 英文关键词: carbon black N134 carbon black N234 TBR tire tread compound anti-reversion agent wear resistance |
| 基金项目: |
| 中图分类号: |
|
| 摘要点击次数: 1546 |
| 全文下载次数: 1103 |
| 中文摘要: |
| 研究新工艺超耐磨炭黑N134替代中超耐磨炭黑N234在全钢载重子午线轮胎胎面胶中的应用。结果表明：采用炭黑N134替代炭黑N234，并加入抗硫化返原剂，胎面胶的磨耗量大幅减小，撕裂强度大幅提高，其他物理性能有所改善；成品轮胎的耐磨性能提高，平均单耗里程超过17000 km·mm-1，轮胎使用寿命延长。 |
| 英文摘要: |
| The super abrasion furnace carbon black N134 prepared by new processing technology was applied in the tread compound of TBR tire and compared with carbon black N234.In the formulation，the anti-reversion agent was added.Compared with N234，the abrasion loss of the vulcanizates with N134 decreased significantly，the tear strength increased remarkably，and other physical properties were improved.With N134 in the tread compound，the abrasion resistance of the finished tire was improved and the service life of the tire was extended showing an average mileage over 17000 km·mm-1. |
|
|