| 橡胶隔离剂C-66的制备及性能研究 |
| Preparation and Properties of Rubber Release Agent C-66 |
| |
| DOI： |
| 中文关键词: 橡胶 隔离剂 胶片 |
| 英文关键词: rubber release agent rubber sheet |
| 基金项目: |
| 中图分类号: |
|
| 摘要点击次数: 1359 |
| 全文下载次数: 1483 |
| 中文摘要: |
| 介绍新型橡胶隔离剂C-66的制备工艺及其对胶片的隔离效果。结果表明：隔离剂C-66常温下易分散于水相，悬浮稳定性优，消泡速度快，制备工艺简单；浸泡隔离剂C-66的胶片风干速度快，附着物分散均匀，叠放胶片无粘连现象，隔离效果良好；隔离剂C-66对胶料性能无不良影响。 |
| 英文摘要: |
| The preparation process of new rubber release agent C-66 was introduced and the release performance was evaluated. The experimental results showed that C-66 could be easily dispersed in water at room temperature， with excellent stability and fast defoaming speed. After the rubber sheet was dipped in the aqueous dispersion of C-66， it dried quickly and the release agent was uniformly deposited. C-66 prevented the rubber sheets from sticking during storage， was well tolerated by the rubber and there was no influence on flow properties or other compound properties during vulcanization. |
|
|
查看全文
查看/发表评论 下载PDF阅读器 |