| Preparation of Modified Microcrystalline Cellulose and Its Effect on Properties of SBR |
| |
| DOI： |
| Key Words: microcrystalline cellulose；modified microcrystalline cellulose；SBR；physical property |
| Author Name | Affiliation | | LU Xuan | Guangdong University of Technology | | Chen Fu-lin | Guangdong University of Technology | | BAI Er-lei | Daikin Fluorine Chemical Co.，Ltd | | CEN Lan | Guangdong University of Technology | | ZHOU Yan-hao | Guangdong University of Technology |
|
| Hits: 855 |
| Download times: 514 |
| Abstract: |
| The properties of microcrystalline cellulose（MCC）and modified microcrystalline cellulose（MMCC）filled SBR were studied. The results showed that，when the addition levels of MCC and MMCC were 20 phr，the SBR vulcanizates had maximum tensile strength（15.3 and 19.0 MPa，espectively）.Compared with the MCC filled SBR vulcanizate.the Akron abrasion loss of MMCC filled SBR vulcanizate was 41% lower.The SBR vulcanizates filled with 20 phr MCC and MMCC had a similar glass transition temperature. |
|
View Full Text
View/Add Comment Download reader |
| Close |