| Properties of Graphene Oxide/Carbon Black/ESBR Nanocomposite |
| |
| DOI： |
| Key Words: graphene oxide；carbon black；ESBR；nanocomposite；tread compound；wear resistance |
| Author Name | Affiliation | | CUI Jun-lei | Beijing University of Chemical Technology | | LIU Li | Beijing University of Chemical Technology | | MAO Ying-yan | Beijing University of Chemical Technology | | WEN Shi-peng | Beijing University of Chemical Technology | | ZHANG Li-qun | Beijing University of Chemical Technology |
|
| Hits: 833 |
| Download times: 572 |
| Abstract: |
| The graphene oxide/ESBR nanocomposite was prepared by emulsion intercalation me thod，and its application in the tread compound of off the road tire was investigated.The results showed that，by adding graphene oxide in the tread compound，the t90 of graphene oxide/carbon black/ESBR nanocomposite was extended，the shear storage modulus and storage modulus increased，the glass transition temperature changed little，and the loss peak decreased.The main physical properties and wear resistance were improved. |
|
View Full Text
View/Add Comment Download reader |
| Close |