| Study on formulation of bonding compound of copper-plated steel cord conveyor belt |
| |
| DOI： |
| Key Words: conveyor belt；copper-plated steel cord；bonding compound；pull out force |
| Author Name | Affiliation | | ZHANG Li-hua | Fuxin Huanyu Rubber(Group) Co.，Ltd. | | GAO Xiu-ling | Fuxin Huanyu Rubber(Group) Co.，Ltd. | | GU Bao-jin | Fuxin Huanyu Rubber(Group) Co.，Ltd. | | QU Cheng-dong | Fuxin Huanyu Rubber(Group) Co.，Ltd. | | TONG Bai-chuan | Fuxin Huanyu Rubber(Group) Co.，Ltd. |
|
| Hits: 607 |
| Download times: 1 |
| Abstract: |
| The formulation of bonding compound of copper-plated steel cord reinforced conveyor belt was investigated.The results showed that，the adhesion strength of copper-plated steel cord and rubber was increased by the resorcinol-formaldehyde-silica-cobalt system；the final formulation was as follows：NR 30，SBR 70，carbon black N330 45，silica 15，zinc oxide 9.5，stearic acid 1，aromatic oil 4，antioxidant 4010NA/BLE C 2.5，adhesive RF 3.6，adhesive RA 2.4，cobalt boroacylate 1.2，sulfur 2.7，accelerator NOBS 1.The Shore A hardness of the vulcanizate was 70 degree，the pull out forces of the steel cord before and after aging（150 ℃×150 min） were 1 260 and 1 185 N，respectively. |
|
View Full Text
View/Add Comment Download reader |
| Close |