| Modification of emulsion nano-compounding technology for organo-montmorillonite/SBR |
| |
| DOI： |
| Key Words: SBR；organo-montmorillonite；nano-composite；distance between layers；predispersion |
| Author Name | Affiliation | | HONG Xiao-bin | Science and Technology University of National Defence | | CHEN Yi-min | Science and Technology University of National Defence | | XIE Kai | Science and Technology University of National Defence |
|
| Hits: 898 |
| Download times: 653 |
| Abstract: |
| The technology of montmorillonite/SBR composite prepared by macromolecular emulsion intercalation was modified.The test results showed that the hydrophobic organo montmorillonite，which was predispersed in a low molecular alcoholic mixture，was directly used to prepare organo montmorillonite/SBR nano-composite by emulsion intercalation；the distance between the layers of organo-montmorillonite was extended by adding small amount of water solution of a polymer with hydroxyl to SBR latex，which was beneficial to increase the intercalating power；and the ultrasonic had little effect on the enhancement of polymer intercalation. |
|
View Full Text
View/Add Comment Download reader |
| Close |