| In-situ polymerized nano-PZDMA/POE composite |
| |
| DOI： |
| Key Words: PZDMA；POE；in-situ polymerization；reinforcement；dispersion phase |
| Author Name | Affiliation | | WU She-mao | Beijing University of Chemical Technology | | LU Yong-lai | Beijing University of Chemical Technology | | LIU Li | Beijing University of Chemical Technology | | GU Liang | Beijing University of Chemical Technology | | ZHANG Li-qun | Beijing University of Chemical Technology |
|
| Hits: 1031 |
| Download times: 833 |
| Abstract: |
| The development process and reinforcing mechanism of the nano-dispersion phase structure in the in-situ polymerized nano-PZDMA/POE were investig ated by micro-scopy and thermogravimetric analysis and the dependence of the stress-strain behavior and tensile streng th of PZDMA/POE composite on the temperature was also studied.The results showed that the nano-dispersion phase（PZDMA）was formed by the in-situ polymerization of ZDMA during vulcanization；the higher streng th of PZDMA/POE composite was mainly contributed by the physical adsorption relaxation between nano-PZDMA dispersion phase and POE molecule rather than their chemical adsorption relaxation；and the stress-strain curve of PZDMA/POE composite was quite different from that of carbon black/POE compound，i.e.the PZDMA/POE composite gave the much higher tensile strength at the room temperature in contrast to the lower tensile streng th at the elevated temperature when compared to carbon black/POE compound. |
|
View Full Text
View/Add Comment Download reader |
| Close |