| Study on properties of ZDMA/NBR nano-composite |
| |
| DOI： |
| Key Words: ZDMA；NBR；nano-composite；reinforcement |
| Author Name | Affiliation | | ZHAO Yang | Beijing University of Chemical Technology | | FENG Yu-xing | Beijing University of Chemical Technology | | LIU Li | Beijing University of Chemical Technology | | LU Yong-lai | Beijing University of Chemical Technology | | ZHANG Li-qun | Beijing University of Chemical Technology |
|
| Hits: 1226 |
| Download times: 0 |
| Abstract: |
| The static and dynamic properties of ZDMA/NBR nano-composite were investigated and compared to those of C.B. N220/NBR system.The test results showed that the higher Shore A hardness，tensile strength，elongation at break，modulus at 100% elongation and tear strength，better hot air aging property and hot oil resistance of ZDMA/NBR vulcanizate were obtained when compared to those of C.B. N220/NBR vulcanizate；and ZDMA/NBR vulcanizate possessed higher storage modulus and lower dy namic compression heat build-up，but larger dynamic compression set. |
|
View Full Text
View/Add Comment Download reader |
| Close |