| Effect of Silane Coupling Agent IMLV/N330 on Properties of Tread Compound of Aircraft Tire |
| Received:April 24, 2024 Revised:April 24, 2024 |
| DOI：10.12136/j.issn.1000-890X.2024.12.0925 |
| Key Words: silane coupling agent；aircraft tire；tread compound；tear strength；cutting resistance |
| Author Name | Affiliation | E-mail | | ZHU Feilei* | 中国化工集团曙光橡胶工业研究设计院有限公司 | 63208016@qq.com | | LIU Zhengyu | 海装广州局 | | | HUANG Zhiyi | 中国化工集团曙光橡胶工业研究设计院有限公司 | | | WANG Ruitong | 中国化工集团曙光橡胶工业研究设计院有限公司 | | | YU Huaying | 中国化工集团曙光橡胶工业研究设计院有限公司 | | | LIU Rong | 中国化工集团曙光橡胶工业研究设计院有限公司 | |
|
| Hits: 178 |
| Download times: 85 |
| Abstract: |
| A experimental study was conducted on new silane coupling agent IMLV/N330 replacing traditional silane coupling agent Si69 black in the tread compound of aircraft tires.The results showed that using silane coupling agent IMLV/N330 replacing silane coupling adgent si69 and partial carbon，the ulcanization speed of the compound was accelerated，the tear strength and elongation at break increased，the hot air aging resistance，cutting resistance and flexural cracking resistance were improved，the wear resistance changed a little，and the heat generation slightly increased. |
|
View Full Text
View/Add Comment Download reader |
| Close |