文章摘要
Effect of CBp/Carbon Black N330 Blending on Properties of NR Compound
Received:March 31, 2023  Revised:March 31, 2023
DOI:10.12136/j.issn.1000-890X.2025.01.0025
Key Words: CBp;carbon black N330;NR;surface roughness;storage modulus;physical property
Author NameAffiliationE-mail
DONG Hailing Qingdao University of Science and Technology 983864497@qq.com 
YAO Huidan Qingdao University of Science and Technology  
FENG Xincong Qingdao University of Science and Technology  
YANG Huiru Qingdao University of Science and Technology  
LIU Jiwen* Qingdao University of Science and Technology liujiwen@qust.edu.cn 
SUN Chong Qingdao University of Science and Technology  
Hits: 460
Download times: 151
Abstract:
      The effect of of cracked carbon black(CBp)/ carbon black N330 blending on the properties of natural rubber(NR) compound were investigated.The results showed that the specific surface area of carbon black N330 was larger than that of CBp,the ash content was significantly lower than that of CBp,and there was not much difference in the types and contents of carbon functional groups between CBp and carbon black N330.The surface roughness of the vulcanizate with single filler was smaller than that of the vulcanizate with blending fillers,and the surface roughness of the vulcanizate with 50 phr of carbon black N330 was larger than that of the vulcanizate with 50 phr of CBp.As the CBp/carbon black N330 blending ratio increased,bound rubber content of the compound decreased,the storage modulus decreased significantly under small strain,and the crosslinking density,Shore A hardness,tensile stress at given elongation and tear strength of the vulcanizates decreased,while the elongation at break and rebound value increased,the tensile strength changed little,but the wear resistance deteriorated.