| Regulation of Carbon Black by Lamellar Sodium-based Montmorillonite and Its Influence on Properties of NR/SBR Nanocomposite |
| Received:March 07, 2022 Revised:March 07, 2022 |
| DOI：10.12136/j.issn.1000-890X.2023.04.0251 |
| Key Words: lamellar sodium-based montmorillonite；carbon black；segregation behavior；dispersion； NR；SBR；nanocomposite；wear resistance |
| Author Name | Affiliation | E-mail | | Liu Chao | Beijing University of Chemical Technology | 844344565@qq.com | | Wu Xiaohui* | Beijing University of Chemical Technology | wuxiaohui@mail.buct.edu.cn | | Lu Yonglai | Beijing University of Chemical Technology | | | Zhang Liqun | Beijing University of Chemical Technology | |
|
| Hits: 991 |
| Download times: 765 |
| Abstract: |
| Natural rubber（NR）/lamellar sodium-based montmorillonite（Na-MMT），styrene-butadiene
rubber （SBR）/Na-MMT and NR/SBR/Na-MMT masterbatches were prepared by emulsion blending
method，then the corresponding NR/SBR/Na-MMT nanocomposites were prepared，and the effect of Na-
MMT on the microscopic morphology，physical properties and wear resistance of the NR/SBR/Na-MMT
nanocomposites was investigated. The results showed that the dispersion of Na-MMT in the NR/SBR/Na-
MMT nanocomposites prepared by using the NR/Na-MMT masterbatch was the best，and the proportion of
Na-MMT in the exfoliated state was the largest，the dispersion of carbon black was also obviously improved，
and the lamellar Na-MMT could regulate the segregation behavior of carbon black in the NR/SBR/Na-
MMT nanocomposites to a certain extent. As a result，the tensile strength，stress at constant elongation and
elongation at break of the NR/SBR/SBR/Na-MMT nanocomposites were the largest，the Akron abrasion
was the smallest（0. 177 cm3），and the grooves on the worn surface was shallowest，showing the best wear
resistance. |
|