Study on Correlation between Structure Parameters and Mechanical Properties of HNBR Based on RPA
Received:November 02, 2020  Revised:November 02, 2020
DOI：10.12136/j.issn.1000-890X.2021.09.0643
Key Words: RPA；HNBR；hydrogenation degree；acrylonitrile content；Mooney viscosity；mechanical property
Author NameAffiliationE-mail
XUE　Yan* Yangzhou University 18463750770@163.com 
XU Xiangrong Yangzhou University  
HUANG　Hao Yangzhou University  
XIE An Yangzhou Heli Rubber Co.，Ltd  
XU Jinxiang Yangzhou University  
ZHANG　Ming Yangzhou University  
Hits: 948
Download times: 756
Abstract:
      The properties of different grades of hydrogenated nitrile rubber(HNBR) compounds and vulcanizates were characterized by rubber processing analyzer(RPA)，and compared with other testing instruments. The results showed that the curing rate and filler dispersion of HNBR compound and mechanical properties of HNBR vulcanizate increased with the increase of the Mooney viscosity of HNBR. The aging resistance of HNBR vulcanizate increased with the increase of the hydrogenation degree of HNBR. The loss factor and glass transition temperature of HNBR vulcanizate increased with the increase of the acrylonitrile content of HNBR. RPA could be used to obtain the test results that usually required multiple instruments，such as rotorless vulcanizer，universal material testing machine，scanning electron microscope and dynamic mechanical analyzer. Therefore，RPA could be used to conveniently regulate the compound formulation of HNBR with different grades to obtain the expected results.