| Preparation of GO/XNBR Nanocomposite and Study on Its Organic Solvent Impermeability |
| Received:June 01, 2020 Revised:June 01, 2020 |
| DOI：10.12136/j.issn.1000-890X.2022.03.0175 |
| Key Words: XNBR；GO；nanocomposite；dispersibility；organic solvent；impermeability |
| Author Name | Affiliation | E-mail | | LI Xiaopeng | Research Institution of Chemical Defense | lxpbuct@163.com | | LI Lei | Research Institution of Chemical Defense | | | ZHAO Yue | Research Institution of Chemical Defense | | | WANG Liying | Research Institution of Chemical Defense | | | LU Lin | Research Institution of Chemical Defense | | | HAN Guolin | Research Institution of Chemical Defense | | | LI Heguo* | Research Institution of Chemical Defense | liheguo1972@126.com |
|
| Hits: 1563 |
| Download times: 931 |
| Abstract: |
| Graphene oxide（GO） was prepared by modified Hummers method，and GO/carboxylated
nitrile rubber（XNBR） nanocomposites were prepared with polyethyleneimine as “bridging molecule”.
The micro morphology，mechanical properties and organic solvents impermeability of the GO/XNBR
nanocomposites were investigated. The results showed that GO and XNBR matrix were bonded well and GO
was uniformly dispersed. The tensile strength of the GO/XNBR nanocomposites increased from 3. 9 MPa
of pure XNBR compound to 7. 2 MPa（GO dosage was 0. 7 phr），which was about 1. 8 times increase. With
the increase of GO dosage，and the organic solvents impermeability time of GO/XNBR nanocomposites was
obviously prolonged. |
|