| Study on Cracking Mechanism of Waste Rubber |
| Received:August 08, 2019 Revised:August 08, 2019 |
| DOI：10.12136/j.issn.1000-890X.2020.09.0664 |
| Key Words: waste rubber；NR；BR；SBR；BIIR；cracking mechanism；thermal analysis；mass loss rate |
| Author Name | Affiliation | E-mail | | YIN Fengfu | Qingdao University of Science and Technology | 871143873@qq.com | | ZHANG Chao* | Qingdao University of Science and Technology | 871143873@qq.com | | ZHUANG Qianxiao | Qingdao University of Science and Technology | | | WANG Chuansheng | Qingdao University of Science and Technology | | | GUO Lei | Qingdao University of Science and Technology | | | XU Yanhui | Qingdao University of Science and Technology | |
|
| Hits: 761 |
| Download times: 136 |
| Abstract: |
| The cracking mechanism of waste rubber was studied by thermogravimetric-derivative thermogravimetric analysis and thermogravimetric-differential scanning analysis of NR，BR，SBR，BIIR and NR/BR/SBR/BIIR blends. The results showed that the cracking reaction process of NR and BIIR was similar，which had only one obvious mass loss process and one peak mass loss rate. The cracking reaction process of BR and SBR was similar，which was divided into two stages. The first stage had a small mass loss，and the second stage had a larger mass loss. The cracking reaction process of NR/BR/SBR/BIIR blends was similar to that of BR，and the characteristic temperature of the cracking reaction was close. |
|
View Full Text
View/Add Comment Download reader |
| Close |