| Caused Analysis of Strength Loss of Dipped Glass Fiber Rope during Vulcanization of Synchronous Belt |
| Received:May 08, 2019 Revised:May 08, 2019 |
| DOI：10.12136/j.issn.1000-890X.2020.01.0069 |
| Key Words: dipped glass fiber rope；synchronous belt；CR；strength loss；vulcanization |
| Author Name | Affiliation | E-mail | | YU Dejiang* | Qingdao Tipont Cord Co. ，Ltd | yudejiang@tianbangcord.com | | JIANG Hua | Qingdao Tipont Cord Co. ，Ltd | | | JIANG Wei | Qingdao Tipont Cord Co. ，Ltd | | | GAO Weisong | Qingdao Tipont Cord Co. ，Ltd | |
|
| Hits: 1489 |
| Download times: 615 |
| Abstract: |
| The reason of strength loss of dipped glass fiber rope during the vulcanization of synchronous belt was analyzed. It was found that when chloroprene rubber（CR） was used as rubber matrix material，the strength loss was significant，since the water and hydrochloric acid produced during CR compound
vulcanization could affect the strength of dipped glass fiber rope，and the strength loss increased with the increase of temperature. |
|