Preparation and Properties of NR/Carbon Black/ Molybdenum Disulfide Composites
Received:December 27, 2018  Revised:December 27, 2018
DOI：10.12136/j.issn.1000-890X.2019.09.0650
Key Words: molybdenum disulfide；NR；carbon black；composite；dispersion；wear resistance；dynamic mechanical property
Author NameAffiliationE-mail
XIE Lina* Beijing Institute of Technology zcj@bit.edu.cn 
FANG Zili ShaanXi Yanchang Petroleum Group Rubber coLTD  
YANG Jiao ShaanXi Yanchang Petroleum Group Rubber coLTD  
GENG Xiaoxiao ShaanXi Yanchang Petroleum Group Rubber coLTD  
ZHU Changjin Beijing Institute of Technology  
LU Ming ShaanXi Yanchang Petroleum Group Rubber coLTD  
CAO Fen ShaanXi Yanchang Petroleum Group Rubber coLTD  
Hits: 1153
Download times: 629
Abstract:
      Molybdenum disulfide（MoS2） nanoparticles were obtained by ultrasonic method，and the natural rubber（NR）/carbon black（CB）/MoS2 composites were prepared by using MoS2 nanoparticles to replace equal amount of CB in the NR/CB composites. The influence of MoS2 on the Panye effect，vulcanization characteristics，physical properties，wear resistance and dynamic mechanical properties of the composites was investigated. The results showed that adding a small amount of MoS2 could improve the filler dispersion. However，when the amount of MoS2 increased，the fillers tended to aggregate again. Payne effect of the composites was weakened by using a small amount of MoS2，the physical properties and wear resistance were enhanced，and the rolling resistance and wet-slip resistance of the composites were only slightly affected. When the amount of MoS2 increased to a large number，the reinforcement was weakened，and the performance of the composites deteriorated.