| Effect of Hot Acid Environment on Properties of Fluororubber |
| Received:March 07, 2018 Revised:March 07, 2018 |
| DOI：10.12136/j.issn.1000-890X.2019.04.0260 |
| Key Words: fluororubber；hydrochloric acid immersion；barium sulfate；thermal performance；tensile property；surface morphology |
| Author Name | Affiliation | E-mail | | CUI Yuguo | School of Materials Science and Engineering,Shenyang University of Chemical Technology,Key Laboratory of Applied Technology of Polymer Materials,the Education Department of Liaoning Province | 771426050@qq.com | | KANG Hailan | School of Materials Science and Engineering,Shenyang University of Chemical Technology,Key Laboratory of Applied Technology of Polymer Materials,the Education Department of Liaoning Province | | | FANG Qinghong* | School of Materials Science and Engineering,Shenyang University of Chemical Technology,Key Laboratory of Applied Technology of Polymer Materials,the Education Department of Liaoning Province | fqh80@126.com |
|
| Hits: 1365 |
| Download times: 414 |
| Abstract: |
| Hot acid immersion corrosion experiments were carried out on fluororubber 246 using hydrochloric acid solution with a mass fraction of 0.05 hydrochloric acid at 80 ℃. The thermal performance，tensile properties and surface morphology of the samples before and after immersion were tested. The results showed that，the hot hydrochloric acid immersion had little influence on the thermal performance of the sample，and the tensile properties decreased. The smooth sample surface became rough from smooth after acid immersion，and holes with different size were formed on the sample surface. The addition of barium sulfate could inhibit the corrosion of hot hydrochloric acid. |
|
View Full Text
View/Add Comment Download reader |
| Close |