| Effect of Carbon Black and Curing Conditions on Properties of Epoxidized ACM |
| |
| DOI： |
| Key Words: ACM；carbon black；curing agent；curing condition；tensile strength；elongation at break |
| Author Name | Affiliation | | LIU Ping | Shanghai Huayi Group Technology Research Institute | | WU Yanan | Shanghai Huayi Group Technology Research Institute | | YU Minqiang | Shanghai Huayi Group Technology Research Institute |
|
| Hits: 396 |
| Download times: 0 |
| Abstract: |
| The effect of the species and addition level of carbon black，addition level of curing agent，curing temperature，curing pressure and curing time on the tensile strength and elongation at break of epoxidized acrylic rubber（ACM） was investigated. The results showed that，when the addition level of carbon black N330 was 55 phr，the addition level of curing agent was 1. 5 phr，the curing temperature was 170 ℃，the curing pressure was 6. 0 MPa，the first-stage curing time was 20 min，and the second-stage curing
time was 2 h，the physical properties of vulcanizate were better. |
|
View Full Text
View/Add Comment Download reader |
| Close |