| Properties of Rice Husk Silica/Carbon Black/NR Composites |
| |
| DOI： |
| Key Words: NR；rice husk silica；carbon black；dynamic mechanical property；low temperature properties；rolling resistance；wet skid resistance |
| Author Name | Affiliation | | LIU Dachen | Shenyang University of Chemical Technology | | WU Xinliang | Shenyang University of Chemical Technology | | TANG Qi | Shenyang University of Chemical Technology | | LI Weishi | Shenyang University of Chemical Technology | | JING Linlin | Shenyang University of Chemical Technology |
|
| Hits: 815 |
| Download times: 372 |
| Abstract: |
| The effect of rice husk silica/carbon black blend on the properties of NR compound was experimentally investigated.The results showed that，when the blending ratio of rice husk silica/carbon black was higher，the ML of the compound was larger，t10 was shorter，t90 was longer，and the physical properties were poorer.When the blending ratio was balanced，the physical properties of the vulcanizate changed little，and the dynamic mechanical property was better.It was also found that the blending ratio had little effect on the low temperature properties of the vulcanizate.When the blending ratio was 20/40 or 25/35，the comprehensive properties of the vulcanizate were better. |
|
View Full Text
View/Add Comment Download reader |
| Close |