| Preparation and Damping Property of Hindered Phenol AO-80/MPU Composite |
| |
| DOI： |
| Key Words: hindered phenol AO-80；MPU；dynamic property；damping property |
| Author Name | Affiliation | | ZHANG Dongyue | Beijing University of Chemical Technology | | CHEN Si | Beijing University of Chemical Technology | | FU Tingwei | Beijing University of Chemical Technology | | LI Junyuan | Beijing University of Chemical Technology | | ZHAO Xiuying | Beijing University of Chemical Technology | | ZHANG Liqun | Beijing University of Chemical Technology |
|
| Hits: 939 |
| Download times: 622 |
| Abstract: |
| A hindered phenol AO-80/MPU composite was prepared by mixing hindered phenol AO-80 into millable polyurethane（MPU），and its properties were investigated.The results showed that the compatibility between hindered phenol AO-80 and MPU was good.As the addition level of hindered phenol AO-80 increased，the glass transition temperature of hindered phenol AO-80/MPU composite gradually increased.Compared with the pure MPU，the physical properties of hindered phenol AO-80/MPU composite decreased，the maximum loss factor increased，the temperature range of effective damping broadened，and the damping property was significantly improved.When the addition level of hindered phenol AO-80 was 40 phr，the damping property and comprehensive physical properties of the composite were optimized. |
|
View Full Text
View/Add Comment Download reader |
| Close |