| Influence of Curing Systems on Properties of NBR/PA6 TPV Prepared by Dynamic Vulcanization |
| |
| DOI： |
| Key Words: NBR；polycaprolactam；thermoplastic vulcanizate；dynamic vulcanization；curing system |
| Author Name | Affiliation | | ZHANG Shi-jia | Beijing University of Chemical Technolog | | WU She-mao | Beijing University of Chemical Technolog | | ZHANG Li-qun | Beijing University of Chemical Technolog |
|
| Hits: 1058 |
| Download times: 370 |
| Abstract: |
| The NBR/polycaprolactam(PA6) thermoplastic vulcanizate(TPV) was prepared by dynamic vulcanization，and the influence of curing systems on the properties of TPV was investigated.The results showed that，compared to curing system using vulcanizing agent HVA-2 and accelerator DM,the TPV prepared by vulcanizing agent SP-1045 and accelerator SnCl2 had better processing and physical properties,and the crystallinity of PA6 was lower. In addition,when the blend ratio of vulcanizing agent HVA-2/accelerator DM was 1.95/0.45 or the blend ratio of vulcanizing agent SP-1045/accelerator SnCl2 was 2.6/0.32,the dispersion phase NBR was in small size and uniformly distributed,and the comprehensive physical properties were good. |
|
View Full Text
View/Add Comment Download reader |
| Close |