| 硫化胶耐磨性能的影响因素分析 |
| Analysis of Factors Affecting Wear Resistance of Vulcanizate |
| Received:May 10, 2023 Revised:May 10, 2023 |
| DOI：10.12137/j.issn.2095-5448.2024.12.0712 |
| 中文关键词: 硫化胶 耐磨性能 老化时间 温度 磨耗角度 磨耗里程 |
| 英文关键词: vulcanizate wear resistance aging time temperature wear angle wear mileage |
| 基金项目: |
| 中图分类号: |
|
| Hits: 174 |
| Download times: 110 |
| 中文摘要: |
| 研究硫化胶耐磨性能的影响因素。结果表明：随老化时间的延长，硫化胶的DIN磨耗量增大，耐磨性能降低；高温下硫化胶的DIN磨耗量大于在常温下的磨耗量；随着磨耗里程的增加，硫化胶的阿克隆磨耗量呈增大趋势；阿克隆试验机的磨耗角度对低炭黑用量胶料的磨耗量影响较大，磨耗角度越大，硫化胶的阿克隆磨耗量越大；湿磨条件下硫化胶的DIN磨耗量远小于干磨条件下的DIN磨耗量。 |
| 英文摘要: |
| The influencing factors of wear resistance of vulcanizete were studied. The results indicated that，with the increase of aging time，the DIN wear of the vulcanizete increased and the wear resistance decreased，the DIN wear of vulcanizete at high temperatures was greater than that at room temperature.With the increase of wear mileage，the Akron wear of vulcanizete showed an increasing trend. The wear angle of the A kron testing machine had a significant impact on the wear amount of low carbon black amount vulcanizates. The larger the wear angle was，the greater the Akron wear of the vulcanizate was. The DIN wear of vulcanizete under wet grinding conditions was much smaller than that under dry grinding conditions. |
|