甲基丙烯酸锌含量对ZSC/HNBR并用胶性能的影响
Effect of ZDMA Content on Properties of ZSC/HNBR Blends
Received:June 27, 2018  Revised:June 27, 2018
DOI:10.12137/j.issn.2095-5448.2019.02.0083
中文关键词: 氢化丁腈橡胶  甲基丙烯酸锌  物理性能
英文关键词: HNBR  ZSC  ZDMA  physical property
基金项目:大学生创新创业训练计划项目(201710424085)
中图分类号:
Author NameAffiliationE-mail
Yang Zhengyi School of Materials Science and Engineering,Shandong University of Science and Technology,266590
579 Qianwangang Road,Huangdao District,Qingdao,shandong 
rlzhit@126.com 
Zhong Sijia School of Materials Science and Engineering,Shandong University of Science and Technology  
Zhang Maoqi School of Materials Science and Engineering,Shandong University of Science and Technology  
Ma Shaoxia* School of Materials Science and Engineering,Shandong University of Science and Technology  
Hits: 2847
Download times: 1130
中文摘要:
      ZSC是甲基丙烯酸锌(ZDMA)接枝改性氢化丁腈橡胶(HNBR)制备的一种新型高强度聚合物。为了提高HNBR胶料在高温下的物理性能,采用机械共混法制备ZSC/HNBR并用胶,通过调整ZSC/HNBR并用比考察ZDMA含量对ZSC/HNBR并用胶性能的影响。结果表明:与纯HNBR硫化胶相比,ZSC/HNBR并用胶的硫化特性、常温及高温物理性能较好;ZDMA含量对ZSC/HNBR并用胶物理性能的影响显著,当ZSC/HNBR并用比为50/50(ZDMA质量分数为0. 245 9)时,硫化胶综合常温物理性能较佳;当ZSC/HNBR并用比为85/15(ZDMA质量分数为0. 423 7)时,硫化胶综合高温物理性能较佳。
英文摘要:
      ZSC is a new type of high strength polymer prepared by grafting modified hydrogenated nitrile rubber(HNBR)with zinc methacrylate(ZDMA).In order to improve the physical properties of HNBR compound at high temperature,ZSC/HNBR blends were prepared by mechanical blending.The effects of ZDMA content on the properties of ZSC/HNBR blends were investigated by adjusting the ZSC/HNBR ratio. The results showed that,ZSC/HNBR blends had better curing characteristics,physical properties at room temperature and high temperature than pure HNBR vulcanizates,and the content of ZDMA had a significant effect on the physical properties of ZSC/HNBR blends.When the blend ratio of ZSC/HNBR was 50/50(the mass fraction of ZDMA was 0.245 9),the comprehensive physical property of the vulcanizate at room temperature was the best.When ZSC/HNBR blend ratio was 85/15(ZDMA mass fraction was 0.423 7), the comprehensive physical property of the vulcanizate at high temperature was the best.