| HOMMT/MVQ纳米复合材料的制备与性能研究 |
| Preparation and properties of HOMMT/MVQ nanocomposite |
| |
| DOI： |
| 中文关键词: 甲基乙烯基硅橡胶 有机蒙脱土 复合材料 超支化技术 耐热性能 |
| 英文关键词: methyl vinyl silicone rubber organic montmorillonite composite hyperbranched technique heat resistance |
| 基金项目:国家自然科学基金青年基金资助项目(50803034)；上海高校知识创新工程建设资助项目（J20904）；上海市重点学科建设资助项目 (J50102) |
|
| 摘要点击次数: 990 |
| 全文下载次数: 0 |
| 中文摘要: |
| 采用超支化技术对有机蒙脱土（OMMT）进行改性制备超支化有机蒙脱土（HOMMT），并制备HOMMT/甲基乙烯基硅橡胶（MVQ）纳米复合材料，对其性能进行研究。结果表明，HOMMT呈剥离纳米片层结构，与OMMT相比，HOMMT耐热性能提高；随着HOMMT用量的增大，HOMMT/MVQ复合材料拉伸强度减小；与MVQ硫化胶相比，当HOMMT用量为1份时，HOMMT/MVQ纳米复合材料拉伸强度提高了28％，拉断伸长率提高了67％，起始降解温度升高了25 ℃。 |
| 英文摘要: |
| A hyperbranched organic montmorillonite(HOMMT) was prepared from modified organic montmorillonite(OMMT) by using hyperbranched technique，then HOMMT/methyl vinyl silicone rubber(MVQ) nanocomposites were prepared，and their properties were investigated.The results showed that，HOMMT exhibited exfoliated and nano scale structure，and the heat resistance of HOMMT was better compared with OMMT was high；the tensile strength of HOMMT/MVQ composite decreased as the addition level of HOMMT increased；the tensile strength and elongation at break of HOMMT/MVQ composite loaded 1 phr HOMMT was improved by 28% and 67% respectively，and the initial thermal degradation temperature was increased by 25 ℃ when compared with MVQ vulcanizate. |
|
|