| 在同步带硫化过程中浸胶玻璃纤维线绳强力损失的原因分析 |
| Caused Analysis of Strength Loss of Dipped Glass Fiber Rope during Vulcanization of Synchronous Belt |
| 投稿时间：2019-05-08 修订日期：2019-05-08 |
| DOI：10.12136/j.issn.1000-890X.2020.01.0069 |
| 中文关键词: 浸胶玻璃纤维线绳 同步带 氯丁橡胶 强力损失 硫化 |
| 英文关键词: dipped glass fiber rope synchronous belt CR strength loss vulcanization |
| 基金项目: |
|
| 摘要点击次数: 1488 |
| 全文下载次数: 613 |
| 中文摘要: |
| 分析浸胶玻璃纤维线绳在同步带硫化过程中强力损失的原因。试验结果表明：浸胶玻璃纤维线绳在以氯丁橡胶（CR）为主体材料的硫化过程中强力损失较大，CR胶料硫化过程中产生的水和盐酸均会对浸胶玻璃纤维线绳的强力产生影响，且随着温度升高，影响愈加明显。 |
| 英文摘要: |
| The reason of strength loss of dipped glass fiber rope during the vulcanization of synchronous belt was analyzed. It was found that when chloroprene rubber（CR） was used as rubber matrix material，the strength loss was significant，since the water and hydrochloric acid produced during CR compound
vulcanization could affect the strength of dipped glass fiber rope，and the strength loss increased with the increase of temperature. |
|
|