| 氯化丁基橡胶/丁腈橡胶宽温域阻尼材料的制备及性能研究 |
| Preparation and Properties of CIIR/NBR Damping Material in Wide Temperature Range |
| 投稿时间：2017-09-01 修订日期：2017-09-01 |
| DOI：10.12136/j.issn.1000-890X.2019.01.0018 |
| 中文关键词: 氯化丁基橡胶 丁腈橡胶 并用胶 树脂 木质纤维素 石墨烯 阻尼温域 |
| 英文关键词: CIIR NBR blend resin lignocellulose graphene damping temperature range |
| 基金项目: |
|
| 摘要点击次数: 1658 |
| 全文下载次数: 689 |
| 中文摘要: |
| 制备氯化丁基橡胶（CIIR）/丁腈橡胶（NBR）宽温域阻尼材料，研究CIIR/NBR并用比以及765树脂、木质纤维素和石墨烯的用量对并用胶阻尼性能的影响。结果表明：当CIIR/NBR并用比为30/70，765树脂、木质纤维素和石墨烯的用量分别为4，10和5份时，并用胶具有较宽的阻尼温域。 |
| 英文摘要: |
| The CIIR/NBR damping material for wide temperature range application was prepared，and the effects of CIIR/NBR blending ratio，the amount of 765 resin，lignocellulose and graphene on the damping properties of the blends were investigated. The results showed that，when the CIIR/NBR blending ratio was 30/70，and the amounts of 765 resin，lignocellulose and graphene were 4，10 and 5 phr，respectively，the blends had a wide damping temperature range. |
|
|