| 高能紫外光降解天然橡胶硫化胶的研究 |
| Study on Degradation of NR Vulcanizate by High Energy Ultraviolet Light |
| |
| DOI： |
| 中文关键词: 紫外光降解 天然橡胶硫化胶 降解机理 溶胶 |
| 英文关键词: ultraviolet light degradation NR vulcanizate degradation mechanism sol |
| 基金项目: |
|
| 摘要点击次数: 1133 |
| 全文下载次数: 619 |
| 中文摘要: |
| 采用高能紫外光反应容器研究天然橡胶（NR）硫化胶的降解过程，探讨NR硫化胶降解程度和溶胶分子结构以及NR硫化胶紫外光降解机理。结果表明：NR硫化胶在高能紫外光照射下能够快速降解，随着照射时间的延长，溶胶质量分数增大，溶胶相对分子质量减小；紫外光照射过程中氧气参与了紫外光降解NR硫化胶过程，使NR硫化胶主链发生断裂，降解产物含有含氧基团，亲水性提高，但随着照射时间的进一步延长，降解产物中的含氧基团继续在紫外光作用下发生反应，含氧基团减少，亲水性降低。 |
| 英文摘要: |
| The degradation process of NR vulcanizate was studied by using high energy ultraviolet light（UV）reaction vessel，and the degradation degree of NR vulcanizate，the molecular structure of sol and the UV degradation mechanism of NR vulcanizate were investigated.The results showed that，NR vulcanizate was degraded quickly under the irradiation of high energy UV，as the exposure time prolonged，sol mass fraction increased，and sol molecular weight decreased. During the UV irradiation process，oxygen was involved in the UV degradation process of NR vulcanizate，the main chain of the NR vulcanizate was broken，the degradation products contained oxygen groups，and the hydrophilic property increased.With further exposure, the oxygen-containing groups in degradation products reacted with other groups under UV irradiation，the content of oxygen groups was reduced，and hydrophilic property decreased. |
|
|
查看全文
查看/发表评论 下载PDF阅读器 |
| 关闭 |