| 沥青基短切碳纤维/导电炭黑/丁腈橡胶复合材料的结构与性能研究 |
| Structure and Properties of Chopped Pitch-Based Carbon Fiber/Conductive Carbon Black/NBR Composite |
| |
| DOI： |
| 中文关键词: 丁腈橡胶 导电炭黑 沥青基短切碳纤维 热导率 导电性能 |
| 英文关键词: NBR conductive carbon black chopped pitch-based carbon fiber thermal conductivity electrical conductivity |
| 基金项目: |
|
| 摘要点击次数: 902 |
| 全文下载次数: 514 |
| 中文摘要: |
| 研究导电炭黑VXC72及沥青基短切碳纤维（CF）用量对丁腈橡胶（NBR）物理性能、导热及导电性能的影响。结果表明，随着导电炭黑VXC72用量的增大，NBR胶料和CF/NBR复合材料的拉伸强度、撕裂强度、定伸应力和热导率逐渐增大，体积电阻率逐渐降低，而且CF/NBR硫化胶的50%、100%定伸应力和热导率比NBR硫化胶有不同程度提高。当导电炭黑VXC72用量相同时，随着CF用量的增大，复合材料的拉伸强度、撕裂强度和拉断伸长率先减小后增大，热导率基本呈线性增加，体积电阻率明显降低。 |
| 英文摘要: |
| The effects of the addition level of conductive carbon black VXC72 and chopped pitch-based carbon fiber（CF） on the mechanical properties，thermal and electrical conductivity of NBR were investigated.The results showed that，with the increase of the addition level of VXC72，the tensile strength，tear strength and thermal conductivity of both VXC72/NBR compound and CF/VXC72/NBR composites increased，while the volume resistivity decreased gradually；while the modulus at 50% elongation, modulus at 100% elongation and thermal conductivity of CF/VXC72/NBR vulcanizate were higher than those of VXC72/NBR vulcanizates，respectively. For the same addition level of VXC72，with the increase of the addition level of CF，the tensile strength，tear strength and elongation at break of the composite first decreased and then increased，while the thermal conductivity almost increased linearly，and volume resistivity decreased significantly. |
|
|
查看全文
查看/发表评论 下载PDF阅读器 |
| 关闭 |