| 改性白炭黑和硅酮粉对丁苯橡胶性能的影响 |
| Effect of Modified Silica and Silicone Powder on Properties of SBR Compound |
| |
| DOI： |
| 中文关键词: 丁苯橡胶 白炭黑 硅酮粉 改性 耐磨性 分散性 |
| 英文关键词: SBR silica silicone powder modification wear resistance dispersion |
| 基金项目: |
|
| 摘要点击次数: 932 |
| 全文下载次数: 571 |
| 中文摘要: |
| 研究改性白炭黑和硅酮粉对丁苯橡胶（SBR）性能的影响。结果表明：在填料用量相同的情况下，随着硅酮粉用量的增大，胶料的ML和MH呈减小趋势，硫化胶的物理性能下降，弹性和耐磨性提高；与末改性填料填充SBR硫化胶相比，硅烷偶联剂KH-550或M-CNSL改性填料填充SBR硫化胶的定伸应力、拉伸强度和拉断伸长率增大，撕裂强度变化不大，弹性和耐磨性提高，其中M-CNSI。的改性效果更明显；扫描电子显微镜分析证明，改性白炭黑和硅酮粉在SBR硫化胶中的分散性提高。 |
| 英文摘要: |
| The effect of modified silica and silicone powder on the properties of SBR compound was investigated. The resultsshowed that，at the same total amount of fillers，as the addition level of silicone powder increased， the MLand MH 0f the compound decreased，the physical properties of the vulcanizates decreased，and the resilience and wear resistance were improved. Compared with the SBR vulcanizate filled with unmodified fillers，the modulus，tensile strength and elongation at break of the SBR vulcanizate filled with fillers modified by silane coupling agent KH-550 0r M-CNSL increased，the tearstrength changed little，and the resilience and wear resistance were improved. It was found that the modification effect of M-CNSL was better. SEM test results indicated that，with modification，the dispersion of silica and silicone powder in the SBR vulcanizate was improved. |
|
|
查看全文
查看/发表评论 下载PDF阅读器 |
| 关闭 |