加工工艺对多官能化丁基橡胶/天然橡胶并用胶性能的影响
Influence of Processing Technology on Properties of MFIIR/NR Blend
  
DOI：
中文关键词: 多官能化丁基橡胶  天然橡胶  并用胶  加工工艺  性能
英文关键词: multifunctional IIR  NR  blend  processing technology  property
基金项目:
作者单位
邵红琪 青岛科技大学 橡塑材料与工程教育部重点实验室；山东省橡塑材料与工程重点实验室 
周晓兰 青岛科技大学 橡塑材料与工程教育部重点实验室；山东省橡塑材料与工程重点实验室 
冯宇 青岛科技大学 橡塑材料与工程教育部重点实验室；山东省橡塑材料与工程重点实验室 
赵季若 青岛科技大学 橡塑材料与工程教育部重点实验室；山东省橡塑材料与工程重点实验室 
冯莺 青岛科技大学 橡塑材料与工程教育部重点实验室；山东省橡塑材料与工程重点实验室 
摘要点击次数: 953
全文下载次数: 481
中文摘要:
      采用不同加工工艺制备多官能化丁基橡胶(MFIIR)/天然橡胶(NR)并用胶，并对其硫化特性、加工性能、物理性能和动态力学性能进行研究。结果表明：采用预硫化工艺后MFIIR/NR并用胶的t10和t90明显延长，表明硫化剂在2种橡胶相中的分散更加均匀；并用胶的物理性能得到改善，拉伸强度、拉断伸长率和撕裂强度明显增大。预硫化后混炼胶在应变为100%时的储能模量增大，硫化胶的Payne效应减弱。预硫化后并用胶的网络结构更加均匀，两种橡胶可以达到很好的共硫化。
英文摘要:
      The multifunctional IIR (MFIIR)/NR blend was prepared by using different processing technology，and the curing behavior，processability，physical properties and dynamic mechanical properties of the blend were investigated.The results showed that，the t10 and t90 of MFIIR/NR blend after prevulcanization were obviously prolonged，indicating that the curing agents were dispersed uniformly in rubber phase.After the prevulcanization process， the physical properties of the blend were improved.Especially，the tensile strength，elongation at break and tear strength increased significantly.The storage modulus at large strain(100%) increased after the prevulcanization，which implied the Payne effect of the vulcanizate was weakened.The network structure of MFIIR/NR blend after prevulcanization was more uniform， and MFIIR and NR could be well co-vulcanized.
Author NameAffiliation
SHAO Hong-qi Qingdao University of Science and Technology/Shandong Provincial Key Laboratory of Rubber-Plastics 
ZHOU Xiao-lan Qingdao University of Science and Technology/Shandong Provincial Key Laboratory of Rubber-Plastics 
FENG Yu Qingdao University of Science and Technology/Shandong Provincial Key Laboratory of Rubber-Plastics 
ZHAO Ji-ruo Qingdao University of Science and Technology/Shandong Provincial Key Laboratory of Rubber-Plastics 
FENG Ying Qingdao University of Science and Technology/Shandong Provincial Key Laboratory of Rubber-Plastics 
查看全文   查看/发表评论  下载PDF阅读器
关闭