| 端基官能化溶聚丁苯橡胶及其复合材料的制备、结构与性能研究 |
| Preparation，structures and properties of end-functionalized SSBR and its composites |
| |
| DOI： |
| 中文关键词: 溶聚丁苯橡胶 白炭黑 烷氧基硅烷 端基官能化 动态性能 |
| 英文关键词: SSBR silica alkoxysilane end-functionalization dynamic properties |
| 基金项目:“十五”国家科技攻关项目(2004BA310A41)；国家自然科学基金资助项目(50573005) |
|
| 摘要点击次数: 851 |
| 全文下载次数: 0 |
| 中文摘要: |
| 采用阴离子聚合方法制备封端率为71%～76%的末端被烷氧基硅烷官能化的溶聚丁苯橡胶(A-SSBR)，研究A-SSBR及白炭黑/A-SSBR复合材料的结构和性能。结果表明，在白炭黑用量相同的条件下，白炭黑/A-SSBR复合材料比白炭黑/SSBR复合材料具有更优异的填料分散性、物理性能、抗湿滑性能和滚动阻力特性；其中A-SSBR与少量白炭黑经加热充分缩合后制备的白炭黑/A-SSBR复合材料各项性能最优。 |
| 英文摘要: |
| The functionalized solution-polymerized styrene-butadiene rubber having alkoxysilane group on chain-ends(A-SSBR) with end-functionalizing efficiency up to 71%～76% was prepared by anionic polymerization.The structures and properties of both A-SSBR and silica/A-SSBR composites were investigated.The results showed that，silica/A-SSBR composites exhibited better filler dispersion，physical properties，wet skid resistance and lower rolling resistance than silica/SSBR composite based on the same silica content.In addition，the properties of the silica/A-SSBR composite prepared by the process of heating-condensation between silica and A-SSBR were at their best. |
|
|
查看全文
查看/发表评论 下载PDF阅读器 |
| 关闭 |