填料-橡胶的化学和物理作用及其对补强的影响
Chemical and physical interactions between filler and rubber and their effect on reinforcement
  
DOI：
中文关键词: 炭黑  白炭黑  NR/BR并用胶  交联密度  补强作用
英文关键词: carbon black  silica  NR/BR blend  crosslinking density  reinforcement
基金项目:国家自然科学基金资助项目(29674013)
作者单位
张士齐 南京理工大学 高分子材料系 
贾红兵 南京理工大学 高分子材料系 
刘卫东 University of Dayton 
摘要点击次数: 944
全文下载次数: 0
中文摘要:
      研究了炭黑N330和白炭黑与NR/BR的相互作用及其对补强的影响。炭黑N330与NR/BR相互作用的化学交联密度占40%，对拉伸强度的贡献率为82.8%；白炭黑/偶联剂KH-846与NR/BR相互作用的化学交联密度占66.7%，对拉伸强度的贡献率为80.7%；炭黑/白炭黑/偶联剂KH-846与NR/BR相互作用的化学交联密度约占70%，对拉伸强度的贡献率约占94%。3种补强体系对拉伸强度的贡献都是化学作用占优势，贡献率超过80%
英文摘要:
      The interactions between filler and rubber and their effect on reinforcement were investiga-ted.The results showed that the chemical crosslinkage accounted for 40% in the interactions between N330 black and NR/BR and its contributive rate to tensile strength was 82.8%；the chemical crosslinkage accounted for 66.7% in the interactions between silica/coupling agent KH-846 and NR/BR and its contributive rate to tensile strength was 80.7%；and the chemical crosslinkage accounted for 70% in the interactions between black/silica/coupling agent KH-846 and NR/BR and its contributive rate to tensile strength was about 94%.The chemical crosslinkage gave prevailing contribution to the tensile strength for all 3 reinforcing systems with over 80% of contributive rate.
Author NameAffiliation
ZHANG Shiqi Nanjing University of Science and Technology 
JIA Hongbing Nanjing University of Science and Technology 
LIU Weidong University of Dayton 
查看全文   查看/发表评论  下载PDF阅读器
关闭