| 共混时间对动态硫化EPDM/PP体系结构与性能的影响 |
| Effect of blending time on structure and properties of dynamically vulcanized EPDM/PP |
| |
| DOI： |
| 中文关键词: EPDM PP 动态硫化 结构 性能 |
| 英文关键词: EPDM PP dynamic vulcanization structure property |
| 基金项目:国家“863”计划资助项目(863-715-012-0160) |
|
| 摘要点击次数: 789 |
| 全文下载次数: 663 |
| 中文摘要: |
| 研究了共混时间对动态硫化EPDM/PP体系结构、静态以及动态力学性能的影响。试验结果表明，随着共混时间的延长，EPDM/PP体系中PP相的结晶度先减小后增大，当共混时间为15 min时，PP相的结晶度最小，PP的晶格结构未变化；EPDM相的交联密度逐渐增大，直至趋于一定值；EPDM的Tg峰向高温区移动；PP的Tg峰变化不明显，其tanδ峰值在共混时间为15 min时最大；共混时间为12 min时EPDM/PP体系的力学性能最佳。 |
| 英文摘要: |
| The effect of the blending time on the structure，the static and dynamic mechanical properties of dynamically vulcanized EPDM/PP blend was investigated.The results showed that the crystallinity of PP phase in the blend decreased at first，and then increased and the crystal structure of PP did not change as the blending time increased；the minimum crystallinity of PP phase was obtained when EPDM/PP was blended fo r 15 min；the crosslink density of EPDM phase increased gradually up to a certain level；the Tg peak of EPDM shifted to the high temperature region；the Tg peak of PP changed little，and its tanδ peak was obtained when EPDM/PP was blended for 15 min；and the optimal mechanical properties of blend were obtained when EPDM/PP was blended for 12 min. |
|
|
查看全文
查看/发表评论 下载PDF阅读器 |
| 关闭 |