| 不同补强体系胶料疲劳断裂性能的研究 |
| Dynamic fatigue and failure characteristics of rubber compounds with different reinforcing fillers |
| |
| DOI： |
| 中文关键词: NR BR 动态疲劳 断裂特性 炭黑补强体系 裂纹 |
| 英文关键词: NR BR dynamic fatigue rupture characteristics carbon black crack |
| 基金项目:国家自然科学基金资助项目（59573002） |
|
| 摘要点击次数: 732 |
| 全文下载次数: 763 |
| 中文摘要: |
| 应用断裂力学理论定性和定量地研究了NR和BR/NR（并用比为70/30）胶料在添加不同炭黑补强体系（HAF，ISAF和SAF）时的动态疲劳过程。用分子论观点描述了胶料的动态疲劳过程，结合断裂特征参数β和C0对S-N曲线进行了分析比较。结果表明，在添加HAF，ISAF和SAF这3种补强体系的胶料中，随着补强体系粒径的减小，其抗裂纹扩展性变差，但胶料内部潜在缺陷减少。 |
| 英文摘要: |
| The dynamic fatigue process of NR and BR/NR（70/30）compounds with different carbon blacks was qualitively and quantitively investigated by using the rupture mechanism. The dynamic fatigue process of rubber compounds was described based on the molecular theory，and the S-N curves were analysed and compared combining with the rupture characteristic parameters β and C0.The results showed that for three different rubber compounds reinforced with HAF，ISAF and SAF respectively，the crack growth resistance deteriorated，but the potential defects in rubber compound decreased as the particle size of carbon black reduced. |
|
|
查看全文
查看/发表评论 下载PDF阅读器 |
| 关闭 |