文章摘要
氯化亚锡对BR/CPE共混物自硫化的影晌
Self-vulcanization of BR/CPE Blend Accelerated by Stannous Chioride
  
DOI：
中文关键词: 自硫化橡胶  BR/CPE共混物  氯化亚锡
英文关键词: self vulcanization  BR/CPE blend  stannous chloride
基金项目:
作者单位
张勇 上海交通大学高分子材料研究所 
章长明 上海交通大学高分子材料研究所 
王平 上海交通大学高分子材料研究所 
张隐西 上海交通大学高分子材料研究所 
摘要点击次数: 685
全文下载次数: 674
中文摘要:
      在BR/CPE自硫化共混物中加人少量氯化亚锡（0.5—2份）能显著促进自硫化反应，增大硫化速度和交联密度，共混物凝胶含量达到98%，进一步增大氯化亚锡用量对共混物硫化和硫化胶性能无显著影响。 BR/CPE共混物用炭黑和白炭黑作补强剂较好．补强剂用量为30份较合适；CPE用量较大，共混物的物理性能较好。
英文摘要:
      The self vulcanization of BR/CPE blend was investigated. It was found that the curing rate and the crosslink density could be significantly increased, and the gel content could reach 98% when the small quantity (0.5-2phr) of stannous chloride was used in the blend. The curing behaviour of blend and the property of vulcanizate were insignificantly influenced when more than 2 phr of stannous chloride was used. 30 phr of carbon black or silica was suitable for the BR/CPE blend. The better physical properties of the vulcanizate could be obtained when CPE was dominant in the blend.
Author NameAffiliation
Zhang Yong Shanghai Jiaotong University 
Zhang Changming Shanghai Jiaotong University 
Wang Ping Shanghai Jiaotong University 
Zhang Yinxi Shanghai Jiaotong University 
查看全文   查看/发表评论  下载PDF阅读器
关闭