丁腈橡胶高温下压缩永久变形的研究
Study on Compression Set of NBR at Elevated Temperature
  
DOI：
中文关键词: 丁腈橡胶N41  压缩永久变形  石英粉  有效硫化体系
英文关键词: NBR N41  compression set  quartz powder  EV system
基金项目:
作者单位
刘毓真 青岛化工学院橡胶工程学院 
郭勇 青岛化工学院橡胶工程学院 
李振明 青岛化工学院橡胶工程学院 
肖建斌 青岛化工学院橡胶工程学院 
摘要点击次数: 688
全文下载次数: 661
中文摘要:
      研究了不同硫化体系和不同无机填料对丁腈橡胶N41在100 ℃高温下的压缩永久变形的影响。结果表明，DTDM有效硫化体系硫化胶的压缩永久变形最小，DCP过氧化物硫化体系次之；CZ有效硫化体系较差；硫黄硫化体系最差。无机填料填充的胶料中，以添加石英粉的胶料压缩永久变形最小，而且用量增加其变形值变化不大。此外是氧化铁红、超细碳酸钙、白炭黑233N和255N。
英文摘要:
      The influence of different curing systems and inorganic fillers on the compression set of NBR N41 at 100 ℃ was studied. The results showed that DTDM EV system was the most effective in terms of the minimum compression set of the vulcanizate；DCP was more effective；CZ EV system was poor；and sulfur curing system was the most poor. Among the inorganic fillers, the quartz filler was the most favourable to the minimum compression set of the vulcanizate, and the compression set would change little with the increase of the quartz filler level；the other favourable inorganic filler were put in the order of iron oxide red ,super-fine calcium carbonate and silica 233N and 255N.
Author NameAffiliation
Liu Yuzhen Qingdao Institute of Chemical Technology 
Guo Yong Qingdao Institute of Chemical Technology 
Li Zhenming Qingdao Institute of Chemical Technology 
Xiao Jianbin Qingdao Institute of Chemical Technology 
查看全文   查看/发表评论  下载PDF阅读器
关闭