高改性溶聚丁苯橡胶对电动汽车轮胎胎面胶性能的影响 |
Effect of Highly Modified Solution Polymerized Styrene Butadiene Rubber on Performance of Electric Vehicle Tire Tread Compound |
Received:September 30, 2022 Revised:September 30, 2022 |
DOI: |
中文关键词: 电动汽车轮胎;溶聚丁苯橡胶;乙烯基;官能化;滚动阻力 |
英文关键词: electric vehicle tire;SSBR;vinyl;functionalization;rolling resistance |
基金项目: |
中图分类号: |
Author Name | Affiliation | E-mail | ZHAO Xiangshuai* | TTA(Qingdao) Tire Technology Co.,Ltd | 36943470@qq.com | LIU Huaqiao | TTA(Qingdao) Tire Technology Co.,Ltd | | GU Peishuang | TTA(Qingdao) Tire Technology Co.,Ltd | | WEI Jianxin | TTA(Qingdao) Tire Technology Co.,Ltd | | ZHU Jiashun | TTA(Qingdao) Tire Technology Co.,Ltd | |
|
Hits: 142 |
Download times: 121 |
中文摘要: |
以在产电动汽车轮胎胎面胶配方为基本配方,分别采用不同牌号的溶聚丁苯橡胶(SSBR)做等量替换,研究SSBR微观结构对胎面胶硫化特性、物理性能和动态力学性能的影响。结果表明,在胶料各项性能相当的前提下,采用乙烯基含量较高的双末端官能化SSBR的胶料具有更低的滞后损失,进而使轮胎的滚动阻力更低。 |
英文摘要: |
Using the tread formula of electric vehicle tire in production as the basic formula,different grades of solution polymerized styrene butadiene rubber(SSBR) were used for equal replacement,the effect of SSBR microstructure on the curing characteristics,physical properties and dynamic mechanical properties of the tread compound were studed.The results showed that under the premise that the properties of the compound were equivalent,the double-end functionalized SSBR with higher vinyl content had lower hysteresis loss,resulting in lower rolling resistance of the tire. |