| 轮胎用耐热空气老化生物基PA56浸胶帘线的粘合性能研究 |
| Study on Adhesion Properties of Bio-based PA56 Dipped Cords for Tires with Hot Air Aging Resistance |
| Received:May 12, 2025 Revised:May 12, 2025 |
| DOI： |
| 中文关键词: 生物基锦纶56；热空气老化；浸胶帘线；粘合性能 |
| 英文关键词: bio-based PA56；PA66；hot air aging；dipped cord；adhesion property |
| 基金项目:江苏省科技计划项目（BM2023419）；扬州市创新联合体建设项目（YZ2025296） |
| 中图分类号: |
| Author Name | Affiliation | E-mail | | XU Tun* | Jiangsu Taiji Industry New Materials Co., Ltd. | xu_tun@163.com | | WANG Xiaolong | Jiangsu Taiji Industry New Materials Co., Ltd. | | | HUA Runjia | Jiangsu Taiji Industry New Materials Co., Ltd. | | | YAN Xuelong | Jiangsu Taiji Industry New Materials Co., Ltd. | | | LIU Min | Jiangsu Taiji Industry New Materials Co., Ltd. | | | XU Qijun | Jiangsu Taiji Industry New Materials Co., Ltd. | |
|
| Hits: 223 |
| Download times: 87 |
| 中文摘要: |
| 研究生物基锦纶（PA）56浸胶帘线和PA66浸胶帘线热空气老化前后的粘合性能。结果表明：采用常规间苯二酚-甲醛-胶乳（RFL）浸渍液的PA浸胶帘线热空气老化后单线剥离粘合性能较差；通过向RFL浸渍液中加入热老化粘合改进剂R和V制得的生物基PA56和PA66浸胶帘线热空气老化后的粘合性能得到显著改善；通过控制浸渍液低固含量制得的耐热空气老化的低附胶量生物基PA56浸胶帘线热空气老化前后均具有良好的粘合性能。 |
| 英文摘要: |
| The adhesion properties of bio-based polyamide 56（PA56） dipped cord and PA66 dipped cord before and after hot air aging were studied.The results showed that the PA dipped cords with conventional resorcinol-formaldehyde-latex（RFL） dipping solution exhibited weak adhesion force in cord and rubber adhesive peeling test（CRA-test） after hot air aging.By adding hot aging adhesion modifiers R and V into the RFL dipping solution，the adhesion properties of bio-based PA56 and PA66 dipped cords after hot air aging were significantly improved in CRA-test.By lower the solid content of the dipping solution，bio-based PA56 dipped cord with low solid contact and hot air aging resistance was prepared，which presented favorable adhesion properties both before and after hot air aging. |
|