直压硫化工艺金属内模电磁感应加热均匀性的试验研究 |
Experimental Study on Electromagnetic Induction Heating Uniformity of Metal Inner Mold in Direct Compression Vulcanization Process |
Received:February 14, 2022 Revised:February 14, 2022 |
DOI:10.12135/j.issn.1006-8171.2023.02.0117 |
中文关键词: 直压硫化内模;电磁感应加热;导磁体;长度;截面尺寸;铁损;温度场 |
英文关键词: direct compressure vulcanized internal mold;electromagnetic induction heating;magnetic conductor;length;section size;iron loss;temperature field |
基金项目:山东省重点研发计划重大科技创新工程 |
中图分类号: |
Author Name | Affiliation | E-mail | JIAo Zhiwei* | Beijing University of Chemical Technology | jiaozw@126.com | SUN Jiale | Beijing University of Chemical Technology | | ZHANG Jinyun | Triangle Tire Co.Ltd. | | WANG Lei | Beijing University of Chemical Technology | | YU Yuan | Beijing University of Chemical Technology | | YAN Hua | Beijing University of Chemical Technology | | YANG Weimin | Beijing University of Chemical Technology | |
|
Hits: 936 |
Download times: 431 |
中文摘要: |
研究导磁体长度和截面尺寸对直压硫化金属内模电磁感应加热均匀性的影响。结果表明:减小导磁体的长度可使得鼓瓦两端磁力线密度下降,使电磁感应加热更均匀,但会导致鼓瓦的加热功率下降,当导磁体长度为170 mm时,直压硫化金属内模电磁感应加热的均匀性最好;增大导磁体的截面尺寸虽然会使得电磁感应加热均匀性有所降低,但可以减小导磁体的涡流损耗和功率损耗,有效解决了导磁体铁损的问题,当导磁体的截面尺寸为20 mm×15 mm时,直压硫化金属内模电磁感应加热效果最好。 |
英文摘要: |
The influence of the length and section size of the magnetic conductor on electromagnetic induction heating uniformity of metal inner mold in direct compression vulcanization was studied.The results showed that reducing the length of the magnetic conductor could reduce the magnetic line density at both ends of the drum pad,and made the electromagnetic induction heating more uniform,but it would lead to a decrease in the heating power of the drum pad.When the length of the magnetic conductor was 170 mm,the electromagnetic induction heating uniformity of metal inner mold in the direct compression vulcanization was the best.Although increasing the section size of the magnetic conductor would reduce the uniformity of electromagnetic induction heating,it could reduce the eddy loss and power loss of the magnetic conductor,effectively solving the problem of iron loss of magnetic conductor. When the section size of the magnetic conductor was 20 mm×15 mm,the effect of electromagnetic induction heating of metal inner mold in direct compression vulcanization was the best. |