| 轿车子午线轮胎带束层胶高硫黄-钴盐粘合体系的研究 |
| Study on high sulfur-cobalt salt adhesion system in belt compound of PCR tire |
| |
| DOI： |
| 中文关键词: 轿车子午线轮胎；带束层胶；粘合体系 |
| 英文关键词: PCR tire；belt compound；adhesion system |
| 基金项目: |
| 中图分类号:U463.341+.4/.6；TQ330.38+7 |
| Author Name | Affiliation | | CHENG Gang | The application of high sulfur-cobalt salt adhesion system in the belt compound of PCR tire was investigated.The results showed that，by using high sulfur-cobalt salt adhesion system in the belt compound of PCR tire，the modulus at 200% and 300% elongation and tensile strength of vulcanizate were increased，the adhesion property between vulcanizate and steel cord was kept，the dynamic property of vulcanizate was improved，the high-speed performance and endurance of finished tire were improved，the production cost was reduced，and the working environment was improved. | | HE Huiying | The application of high sulfur-cobalt salt adhesion system in the belt compound of PCR tire was investigated.The results showed that，by using high sulfur-cobalt salt adhesion system in the belt compound of PCR tire，the modulus at 200% and 300% elongation and tensile strength of vulcanizate were increased，the adhesion property between vulcanizate and steel cord was kept，the dynamic property of vulcanizate was improved，the high-speed performance and endurance of finished tire were improved，the production cost was reduced，and the working environment was improved. | | ZHANG Xiaofei | The application of high sulfur-cobalt salt adhesion system in the belt compound of PCR tire was investigated.The results showed that，by using high sulfur-cobalt salt adhesion system in the belt compound of PCR tire，the modulus at 200% and 300% elongation and tensile strength of vulcanizate were increased，the adhesion property between vulcanizate and steel cord was kept，the dynamic property of vulcanizate was improved，the high-speed performance and endurance of finished tire were improved，the production cost was reduced，and the working environment was improved. |
|
| Hits: 604 |
| Download times: 21 |
| 中文摘要: |
| 研究高硫黄-钴盐粘合体系在轿车子午线轮胎带束层胶中的应用。试验结果表明，在轿车子午线轮胎带束层胶中采用高硫黄-钴盐粘合体系，可以提高硫化胶的200%和300%定伸应力及拉伸强度，保持硫化胶与钢丝帘线的粘合性能，提高硫化胶的动态力学性能及成品轮胎的高速性能和耐久性能，降低生产成本，改善作业环境。 |
| 英文摘要: |
| The application of high sulfur-cobalt salt adhesion system in the belt compound of PCR tire was investigated.The results showed that，by using high sulfur-cobalt salt adhesion system in the belt compound of PCR tire，the modulus at 200% and 300% elongation and tensile strength of vulcanizate were increased，the adhesion property between vulcanizate and steel cord was kept，the dynamic property of vulcanizate was improved，the high-speed performance and endurance of finished tire were improved，the production cost was reduced，and the working environment was improved. |
|