| 新型聚氨酯型粘合剂Kin-U19在航空轮胎芳纶帘布胶中的应用 |
| Application of Novel Polyurethane Adhesive Kin-U19 in Aramid Carcass Ply Compound of Aircraft Tire |
| 投稿时间：2024-03-18 修订日期：2024-03-18 |
| DOI： |
| 中文关键词: 粘合剂Kin-U19 航空轮胎 芳纶帘布胶 H抽出力 物理性能 生热 |
| 英文关键词: adhesive Kin-U19 aircraft tire aramid carcass ply compound H pull out physical property heat build-up |
| 基金项目: |
| 中图分类号: |
|
| 摘要点击次数: 145 |
| 全文下载次数: 75 |
| 中文摘要: |
| 研究新型聚氨酯型粘合剂Kin-U19（简称Kin-U19）在航空轮胎芳纶帘布胶中的应用。结果表明：与空白配方和添加间-甲-白粘合体系配方相比，添加Kin-U19的胶料与芳纶帘线之间的粘合力增大，热氧老化后的H抽出力变化不大，稳定性更好，胶料的焦烧时间延长，加工安全性好，混炼及压延过程中无烟雾产生，有利于环保；硫化胶的硬度、300%定伸应力、拉伸强度和撕裂强度提高，物理性能较好，压缩生热降低，导热系数增大，有利于延长航空轮胎的使用寿命；Kin-U19用量为4份时，胶料的综合性能最优，可等量替代间-甲-白粘合体系；以添加4份Kin-U19的胶料试制某型号航空轮胎，成品轮胎帘布的层间粘合强度增大。 |
| 英文摘要: |
| Application of a novel polyurethane adhesive Kin-U19（refferred to as Kin-U19） in aramid carcass ply compound of aircraft tires was studied.The results showed that，compared with the blank formula and the formula with added resorcinol-formaldehyde resin-silica adhesive system，the adhesive force between the compound added Kin-U19 and the aramid cord increased，the H pull out after thermal oxidative aging did not change much，the stability was better，the scorch time was prolonged，the processing safety was good，and there was no smoke generated during mixing and rolling，which was beneficial to environmental protection.The hardness，300% elongation，tensile strength and tear strength of the vulcanizate were improved，and the physical properties were better，compression heat build-up was reduced，and the thermal conductivity was increased，which was beneficial for extending the service life of aircraft tires.When the dosage of Kin-U19 was 4 phr，the comprehensive performance of the adhesive was optimal，and it could replace the resorcinol-formaldehyde resin-silica adhesive system equally.Trial production of a certain model of aircraft tire with the addition of 4 phr Kin-U19 resulted in an increase in interlayer adhesive strength of the finished tire carcass ply. |
|
|