| 胎圈钢丝与胶料脱层问题分析 |
| Analysis of Delamination between Bead Wire and Compound |
| 投稿时间：2021-08-05 修订日期：2021-08-05 |
| DOI：10.12135/j.issn.1006-8171.2022.04.0248 |
| 中文关键词: 胎圈钢丝 钢丝镀层 胶料 脱层 粘合力 表面形貌 |
| 英文关键词: bead wire wire coating compound delamination adhesion surface topography |
| 基金项目: |
| 中图分类号: |
|
| 摘要点击次数: 1056 |
| 全文下载次数: 621 |
| 中文摘要: |
| 利用扫描电子显微镜等分析设备从不同方面分析轮胎胎圈钢丝与胶料脱层问题。结果表明，胎圈钢丝与胶料脱层原因可能是钢丝表面损伤或者钢丝表面镀层不均匀，通过加强质量管控，做好钢丝镀层质量及成分的监控以及钢丝镀层损伤和均匀性的监控，可以有效解决胎圈钢丝与胶料脱层问题。 |
| 英文摘要: |
| The delamination between tire bead wire and compound was analyzed from different aspects by using scanning electron microscope and other analysis equipment.The results showed that the reason for the delamination between bead wire and compound might be the damage of wire surface or the uneven coating on wire surface.The delamination between bead wire and compound could be effectively solved by strengthening quality control，monitoring the quality and composition of wire coating，and monitoring the damage and uniformity of wire coating. |
|
|