| 后硫化稳定剂HTS在带束层胶中的应用研究 |
| Application of Post-vulcanization Stabilizer HTS in Belt Compound |
| 投稿时间：2021-04-01 修订日期：2021-04-01 |
| DOI： |
| 中文关键词: 后硫化稳定剂HTS 带束层胶 弹性模量 抗撕裂性能 粘合强度 |
| 英文关键词: post-vulcanization stabilizer HTS belt compound elastic modulus tear resistance adhesive strength |
| 基金项目: |
| 中图分类号: |
|
| 摘要点击次数: 580 |
| 全文下载次数: 479 |
| 中文摘要: |
| 研究不同炼胶工艺条件下后硫化稳定剂HTS对带束层胶性能以及胶料与钢丝帘线粘合强度的影响。结果表明：加入后硫化稳定剂HTS可以明显提高胶料的弹性模量；混炼时的温度对后硫化稳定剂HTS的活性有较大影响，在145 ℃活化温度下，胶料老化前后的抗撕裂性能最佳，与钢丝帘线的粘合强度也达到最大值。 |
| 英文摘要: |
| The effects of the post-vulcanization stabilizer HTS on the properties of belt compound and the adhesive strength of compound to steel cord under different mixing process conditions were studied.The results showed that the addition of post-vulcanization stabilizer HTS could significantly increase the elastic modulus of compound，the temperature during mixing had a greater influence on the activity of post-vulcanization stabilizer HTS.At the activation temperature of 145 ℃，the tear resistance of compound before and after aging were the best，and the adhesive strength of compound to steel cord also reached the maximum. |
|
|