| 跑气保用轮胎支撑胶流动性对挤出破边的影响 |
| Effect of Fluidity of Run-flat Tire Support Compound on Extrusion Edge Breaking |
| 投稿时间：2020-08-11 修订日期：2020-08-11 |
| DOI：10.12135/j.issn.1006-8171.2021.06.0384 |
| 中文关键词: 跑气保用轮胎 支撑胶 流动性 挤出破边 酚醛增粘树脂 |
| 英文关键词: run-flat tire support compound liquidity extrusion edge breaking phenolic resin |
| 基金项目: |
| 中图分类号: |
|
| 摘要点击次数: 1083 |
| 全文下载次数: 659 |
| 中文摘要: |
| 在工业化生产条件下通过使用不同流动性的胶料，研究胶料流动性对跑气保用轮胎支撑胶挤出破边的影响。研究结果表明，在相同混炼工艺条件下，加入2份酚醛增粘树脂并减少0.5份抗硫化返原剂，胶料的硫化速度加快、焦烧时间缩短、综合物理性能相当，流动性提高30%左右。在相同挤出工艺条件下，提高胶料流动性可明显改善支撑胶挤出破边现象。 |
| 英文摘要: |
| Under the condition of industrial production，the influence of compound fluidity on extrusion edge breaking of run-flat tire support compound was studied.The results showed that under the same mixing process，adding 2 phr phenolic resin and reducing 0.5 phr anti-reversion agent，the curing speed of compound was accelerated，the scorch time was shortened，the comprehensive physical properties were equivalent，and the fluidity was increased by about 30%.Under the same extrusion process，increasing the fluidity of compound could improve the extrusion edge breaking phenomenon of support compound significantly. |
|
|