杨振林,王才朋,李云峰,陈宝喜.配合剂预分散母胶粒在天然橡胶中分散均匀性的研究[J].橡胶科技,2017,15(7):33-36. |
 二维码(扫一下试试看!) |
配合剂预分散母胶粒在天然橡胶中分散均匀性的研究 |
Study on Dispersion Uniformity of Additive Pre-dispersed Masterbatch in Natural Rubber |
|
DOI: |
中文关键词: 预分散母胶粒 硫黄 促进剂 防焦剂 天然橡胶 分散性 门尼粘度 |
英文关键词: pre-dispersed masterbatch sulfur accelerator anti-scorching agent natural rubber dispersion Mooney viscosity |
基金项目: |
中图分类号:TQ330.38+7;TQ332 |
|
摘要点击次数: 1103 |
全文下载次数: 535 |
中文摘要: |
研究硫黄、促进剂CBS和防焦剂CTP预分散母胶粒(牌号分别为S-80,CBS-80和CTP-80,有效成分质量分数均为0.8)门尼粘度和活性成分粒径对其在天然橡胶中分散均匀性的影响。结果表明:低门尼粘度配合剂预分散母胶粒的分散性较好;混炼胶门尼粘度较低时,高门尼粘度配合剂预分散母胶粒分散性较差;增大混炼程度可提高配合剂预分散母胶粒在胶料中的分散性,但无法彻底消除活性成分粒径对配合剂母胶粒分散性的影响。 |
英文摘要: |
In this study,the influence of the Mooney viscosity and active ingredient particle size of the additive pre-dispersed masterbatch,for example,sulfur,accelerator CBS and anti-scorching agent CTP pre-dispersed masterbatch which were referred to as S-80,CBS-80 and CTP-80 and all had effective additive content of 0. 8,on the dispersion of the additive pre-dispersed materbatch in the natural rubber(NR) compound was investigated. The results showed that the dispersion of the additive pre-dispersed masterbatch with lower Mooney viscosity was better. When the Mooney viscosity of the NR compound was low,the dispersion of the additive pre-dispersed materbatch with higher Mooney viscosity was poor. The dispersion of the additive pre-dispersed materbatch could be improved by increase of mixing intensity;however,the effect of the particle size of active ingredient could not be completely eliminated. |
|