| 多功能助交联剂CA94-50在三元乙丙橡胶中的应用 |
| Application of Multifunctional Auxiliary Crosslinking Agent CA94-50 in EPDM |
| Received:September 22, 2020 Revised:September 22, 2020 |
| DOI：10.12137/j.issn.2095-5448.2021.02.0079 |
| 中文关键词: 三元乙丙橡胶；助交联剂；硫化速度；物理性能 |
| 英文关键词: EPDM；auxiliary crosslinking agent；curing speed；physical property |
| 基金项目: |
| 中图分类号: |
| Author Name | Affiliation | E-mail | | CHE Yongxing* | CRI | 2903154335@qq.com | | ZHANG Xiaolian | Marine Chemical Research Institute Co.，Ltd | |
|
| Hits: 1239 |
| Download times: 4 |
| 中文摘要: |
| 研究多功能助交联剂CA94-50在三元乙丙橡胶（EPDM）中的应用。结果表明，相较于添加助交联剂TAIC-70，SR350和Ricon 153D的胶料，添加多功能助交联剂CA94-50的EPDM胶料的焦烧时间较长，硫化速度和交联程度提高，硫化胶的硬度、100%定伸应力、拉伸强度和拉断伸长率较高，与金属的粘合强度较大，热氧老化后性能变化不大。 |
| 英文摘要: |
| The application of multifunctional auxiliary crosslinking agent CA94-50 in Ethylene Propylene Diene Monomer（EPDM）.The results showed that，compared with the compound with the addition of auxiliary crosslinking agents TAIC-70，SR350 and Ricon 153D，the scorch time of compound with auxiliary crosslinking agent CA94-50 was prolonged，the curing speed and crosslinking degree were improved，and the hardness，modulus at 100% elongation，tensile strength and elongation at break of the vulcanizate were higher，the adhesive strength with metal was larger，and the properties were changed little after thermal oxidation aging. |
|