| 端羟基液体氟26橡胶的制备与应用研究 |
| Preparation and Application of Hydroxyl Terminated Liquid Fluororubber 26 |
| |
| DOI： |
| 中文关键词: 端羟基液体氟橡胶；端羧基液体氟橡胶；氢化丁腈橡胶；遥爪聚合物；催化体系；耐油性能 |
| 英文关键词: hydroxyl terminated liquid fluororubber； carboxyl terminated liquid fluororubber； HNBR；telechelic polymer； catalyst system； oil resistance |
| 基金项目: |
| 中图分类号: |
| Author Name | Affiliation | | Wu Meng | State Key Laboratory of Organic-Inorganic Composites，Beijing University of Chemical Technology | | Qi Shicheng | State Key Laboratory of Organic-Inorganic Composites，Beijing University of Chemical Technology；Key Laboratory of Carbon Fiber and Functional Polymers，Beijing University of Chemical Technology | | Wang Kaiwen | State Key Laboratory of Organic-Inorganic Composites，Beijing University of Chemical Technology | | Zhang Liqun | State Key Laboratory of Organic-Inorganic Composites，Beijing University of Chemical Technology | | Yue Dongmei | State Key Laboratory of Organic-Inorganic Composites，Beijing University of Chemical Technology |
|
| Hits: 922 |
| Download times: 717 |
| 中文摘要: |
| 研究端羟基液体氟26橡胶的制备与应用。用硼氢化钾/稀硫酸体系作催化剂对端羧基液体氟26橡胶进行还原制得遥爪聚合物端羟基液体氟26橡胶。分别以端羟基液体氟26橡胶和端羧基液体氟26橡胶作为增塑剂制备氢化丁腈橡胶（HNBR）胶料。结果表明，2种液体氟26橡胶与HNBR的相容性好，加入端羟基液体氟26橡胶的胶料物理性能、耐老化性能以及耐ASTM 1#油性能较好。 |
| 英文摘要: |
| In this study，the hydroxyl terminated liquid fluororubber 26 was prepared and its application was investigated.The hydroxyl terminated rubber was prepared by reduction reaction of carboxyl terminated precedent using potassium borohydride/sulfuric acid as catalyst system.The hydroxyl terminated fluororubber 26 and carboxyl terminated fluororubber 26 were then applied in HNBR as plasticizers，respectively.It was found both liquid fluororubbers showed good compatibility with HNBR.The physical properties，aging resistance and resistance to ASTM 1# oil of the HNBR vulcanizates with hydroxyl terminated liquid fluororubber 26 were better. |
|