| Application of Carbon Black V10H in Tread Compound of Steel-belted Radial Tire |
| Received:December 31, 2019 Revised:January 02, 2020 |
| DOI：10.12135/j.issn.1006-8171.2021.02.0094 |
| 中文关键词: 炭黑；半钢子午线轮胎；胎面胶；耐磨性能；高速性能；耐久性能 |
| 英文关键词: carbon black；steel-belted radial tire；tread compound；wear resistance；high speed performance；durability |
| 基金项目: |
| 中图分类号: |
| Author Name | Affiliation | E-mail | | XIANG Chundong* | Sichuan Haida Rubber Group Co.,Ltd. | | | LI Zhenting | Sichuan Haida Rubber Group Co.,Ltd. | | | ZHANG Junwei | Sichuan Haida Rubber Group Co.,Ltd. | zhangjunwei@hdtyre.com | | WANG Qiang | Sichuan Haida Rubber Group Co.,Ltd. | wangqiang@hdtyre.com | | DONG Jixue | Sichuan Haida Rubber Group Co.,Ltd. | | | LUO Jiangang | Sichuan Haida Rubber Group Co.,Ltd. | | | LI Dong | Sichuan Haida Rubber Group Co.,Ltd. | | | WANG Tinghua | Sichuan Haida Rubber Group Co.,Ltd. | | | DAI Mingli | Sichuan Haida Rubber Group Co.,Ltd. | |
|
| Hits: 815 |
| Download times: 425 |
| 中文摘要: |
| 研究炭黑V10H在半钢子午线轮胎胎面胶中的应用。结果表明：在半钢子午线轮胎胎面胶中以炭黑V10H减量替代炭黑N234，胶料的门尼粘度减小，门尼焦烧时间延长，硫化速率稍小，硫化胶的拉伸强度、拉断伸长率和撕裂强度增大，耐磨性能显著提高，成品轮胎的高速和耐久性能均明显提高。 |
| 英文摘要: |
| The application of carbon black V10H in the tread compound of steel-belted radial tire was studied.The results showed that，by using carbon black V10H instead of carbon black N234 with reducing dosage in the tread compound of steel-belted radial tire，the Mooney viscosity of the compound decreased，the Mooney scorch time prolonged and the cure rate was slightly smaller.The tensile strength，elongation at break and tear strength of the vulcanizate increased，the wear resistance increased significantly.The high speed performance and durability of the finished tire increased significantly. |
|